Condensed Matter > Materials Science

Title: Nanostrucure of Hybrid Plasmonic-Potonic Crystal Formed on Gel-Immobilized Colloidal Crystal Observer by AFM after Drying

Abstract: Aiming at fabrication of hybrid plasmonic-photonic crystals, gel-immobilized colloidal crystals made of a polystyrene colloidal suspension and an N-(Hydroxy methyl)acrylamid-based gel were immersed into an aqueous dispersion of gold nanoparticles. Atomic force microscope (AFM) observations have been performed for the gel-immobilized colloidal crystals with gold nanoparticles deposited on their surfaces. In the present study, the diameter of a colloidal sphere was c.a. 190 nm. The diameter of a gold nanoparticle was the same as in a preliminary study, c.a. 40 nm. Various immersion times up to two hours were tested. Surface of a sample of 2 hr immersion has been observed. Prior to the AFM observation, the sample was dried in a desiccator for 18 hrs. We have identified a face-centered cubic {111} structure of a colloidal crystal of nearly close packing. Nanoparticles isolated with one another have been observed on the surface of gel-immobilized crystal, which can be regarded as gold nanoparticles from their sizes.
Comments: 29 pages, 8 figures, 1 table; Bulletin of Chemical Society of Japan, accepted
Subjects: Materials Science (cond-mat.mtrl-sci); Soft Condensed Matter (cond-mat.soft); Chemical Physics (physics.chem-ph)
Journal reference: Bulletin of the Chemical Society of Japan, Vol. 89, No. 3, pp. 385--393 (2016)
DOI: 10.1246/bcsj.20150281
Cite as: arXiv:1512.00985 [cond-mat.mtrl-sci]
  (or arXiv:1512.00985v1 [cond-mat.mtrl-sci] for this version)

Submission history

From: Atsushi Mori [view email]
[v1] Thu, 3 Dec 2015 08:34:14 GMT (917kb)

Link back to: arXiv, form interface, contact.