Title: Flexural Fatigue Life of Woven Carbon/Vinyl Ester Composites under Sea Water Saturation

Abstract: The adverse effects of sea water environment on the fatigue life of woven carbon fiber/vinyl ester composites are established at room temperature in view of long-term survivability of offshore structures. It is observed that the influence of sea water saturation on the fatigue life is more pronounced when the maximum cyclic displacement approaches maximum quasi-static deflection, that is, the reduction in the number of cycles to failure are comparable between dry and sea water saturated samples at lower strain ranges (~37% at 0.46% strain), but are drastically different at higher strain ranges (~90% at 0.62% strain). Key damage modes that manifest during the fatigue loading is also identified, and a non-linear model is established for predicting low cycle fatigue life of these composites in dry and sea water saturated conditions.
Subjects: Applied Physics (physics.app-ph)
DOI: 10.1016/j.ijfatigue.2020.105641
Cite as: arXiv:1911.08665 [physics.app-ph]
  (or arXiv:1911.08665v2 [physics.app-ph] for this version)

Submission history

From: Pavana Prabhakar [view email]
[v1] Wed, 20 Nov 2019 01:59:13 GMT (3131kb,D)
[v2] Mon, 6 Apr 2020 16:50:01 GMT (9609kb,D)

Link back to: arXiv, form interface, contact.