Title: Flexural Fatigue Life of Woven Carbon/Vinyl Ester Composites under Sea Water Saturation
(Submitted on 20 Nov 2019 (v1), last revised 6 Apr 2020 (this version, v2))
Abstract: The adverse effects of sea water environment on the fatigue life of woven carbon fiber/vinyl ester composites are established at room temperature in view of long-term survivability of offshore structures. It is observed that the influence of sea water saturation on the fatigue life is more pronounced when the maximum cyclic displacement approaches maximum quasi-static deflection, that is, the reduction in the number of cycles to failure are comparable between dry and sea water saturated samples at lower strain ranges (~37% at 0.46% strain), but are drastically different at higher strain ranges (~90% at 0.62% strain). Key damage modes that manifest during the fatigue loading is also identified, and a non-linear model is established for predicting low cycle fatigue life of these composites in dry and sea water saturated conditions.
Submission history
From: Pavana Prabhakar [view email][v1] Wed, 20 Nov 2019 01:59:13 GMT (3131kb,D)
[v2] Mon, 6 Apr 2020 16:50:01 GMT (9609kb,D)
Link back to: arXiv, form interface, contact.