Title: Magnetic properties of Co/Ni-based multilayers with Pd and Pt insertion layers

Abstract: In this study, the influence of Pd and Pt insertion layers in Co/Ni multilayers (MLs) on their magnetic properties, e.g. magnetic anisotropies, saturation magnetization, coercivity, magnetic domain size, and Curie temperature, is investigated. We compare three series of [Co/Ni/X]N ML systems (X = Pd, Pt, no insertion layer), varying the individual Co layer thickness as well as the repetition number N. All three systems behave very similarly for the different Co layer thicknesses. For all systems, a maximum effective magnetic anisotropy was achieved for MLs with a Co layer thickness between 0.15 nm and 0.25 nm. The transition from an out-of-plane to an in-plane system occurs at about 0.4 nm of Co. While [Co(0.2 nm)/Ni(0.4 nm)]N MLs change their preferred easy magnetization axis from out-of-plane to in-plane after 6 bilayer repetitions, insertion of Pd and Pt results in an extension of this transition beyond 15 repetitions. The maximum effective magnetic anisotropy was more than doubled from 105 kJ/m3 for [Co/Ni]3 to 275 and 186 kJ/m3 for Pt and Pd, respectively. Furthermore, the insertion layers strongly reduce the initial saturation magnetization of 1100 kA/m of Co/Ni MLs and lower the Curie temperature from 720 to around 500 K
Subjects: Materials Science (cond-mat.mtrl-sci)
Cite as: arXiv:2003.14306 [cond-mat.mtrl-sci]
  (or arXiv:2003.14306v1 [cond-mat.mtrl-sci] for this version)

Submission history

From: Michael Heigl [view email]
[v1] Tue, 31 Mar 2020 15:46:21 GMT (700kb,D)

Link back to: arXiv, form interface, contact.