Title: Processes associated with ionic current rectification at a 2D-titanate nanosheet deposit on a microhole poly (ethylene terephthalate) substrate

Abstract: Films of titanate nanosheets (approx. 1.8-nm layer thickness and 200-nm size) having a lamellar structure can form electrolytefilled semi-permeable channels containing tetrabutylammonium cations. By evaporation of a colloidal solution, persistent deposits are readily formed with approx. 10 micrometer thickness on a 6-micrometer-thick poly(ethylene-terephthalate) (PET) substrate with a 20 micrometer diameter microhole. When immersed in aqueous solution, the titanate nanosheets exhibit a p.z.c. of -37 mV, consistent with the formation of a cation conducting (semi-permeable) deposit. With a sufficiently low ionic strength in the aqueous electrolyte, ionic current rectification is observed (cationic diode behaviour). Currents can be dissected into (i) electrolyte cation transport, (ii) electrolyte anion transport and (iii) water heterolysis causing additional proton transport. For all types of electrolyte cations, a water heterolysis mechanism is observed. For Ca2+ and Mg2+ ions, water heterolysis causes ion current blocking, presumably due to localised hydroxide-induced precipitation processes. Aqueous NBu4+ is shown to invert the diode effect (from cationic to anionic diode). Potential for applications in desalination and/or ion sensing are discussed
Subjects: Chemical Physics (physics.chem-ph); Materials Science (cond-mat.mtrl-sci)
DOI: 10.1007/s10008-019-04199-4
Cite as: arXiv:2004.01010 [physics.chem-ph]
  (or arXiv:2004.01010v1 [physics.chem-ph] for this version)

Submission history

From: Christian Harito Dr [view email]
[v1] Thu, 2 Apr 2020 14:03:50 GMT (4705kb)

Link back to: arXiv, form interface, contact.