Title: Low Temperature Homoepitaxy Of (010) $β$-Ga$_2$O$_3$ By Metalorganic Vapor Phase Epitaxy : Expanding The Growth Window
(Submitted on 1 Aug 2020)
Abstract: In this work, we report on the growth of high-mobility $\beta$-Ga$_2$O$_3$ homoepitaxial thin films grown at a temperature much lower than the conventional growth temperature window for metalorganic vapor phase epitaxy. Low-temperature $\beta$-Ga$_2$O$_3$ thin films grown at 600$^{\circ}$C on Fe-doped (010) bulk substrates exhibits remarkable crystalline quality which is evident from the measured room temperature Hall mobility of 186 cm$^2$/Vs for the unintentionally doped films. N-type doping is achieved by using Si as a dopant and controllable doping in the range of 2$\times$10$^{16}$ - 2$\times$10$^{19}$ cm$^{-3}$ is studied. Si incorporation and activation is studied by comparing silicon concentration from secondary ion mass spectroscopy (SIMS) and electron concentration from temperature-dependent Hall measurements. The films exhibit high purity (low C and H concentrations) with a very low concentration of compensating acceptors (2$\times$10$^{15}$ cm$^{-3}$) even at this growth temperature. Additionally, abrupt doping profile with forward decay of $\sim$ 5nm/dec (10 times improvement compared to what is observed for thin films grown at 810$^{\circ}$C) is demonstrated by growing at a lower temperature.
Submission history
From: Arkka Bhattacharyya [view email][v1] Sat, 1 Aug 2020 17:28:47 GMT (1054kb,D)
Link back to: arXiv, form interface, contact.