Title: Why is it so difficult to realize Dy$^{4+}$ in as-synthesized BaZrO$_3$?
(Submitted on 18 Nov 2021 (v1), last revised 17 Feb 2022 (this version, v2))
Abstract: Rare-earth doped barium zirconate (BaZrO$_3$) ceramics are of interest as proton-conducting and luminescent materials. Here, we report a study of dysprosium (Dy) and other relevant point defects in BaZrO$_3$ using hybrid density-functional defect calculations. The tetravalent Dy$^{4+}$ is found to be structurally and electronically stable at the Zr lattice site (i.e., as Dy$_{\rm Zr}^0$), but most often energetically less favorable than the trivalent Dy$^{3+}$ (i.e., Dy$_{\rm Zr}^-$) in as-synthesized BaZrO$_3$, due to the formation of low-energy, positively charged oxygen vacancies and the mixed-site occupancy of Dy in the host lattice. The Dy$^{4+}$/Dy$^{3+}$ ratio can, in principle, be increased by preparing the material under highly oxidizing and Ba-rich conditions and co-doping with acceptor-like impurities; however, post-synthesis treatment may still be needed to realize a non-negligible Dy$^{4+}$ concentration. We also find that certain unoccupied Dy $4f$ states and the O $2p$ states are {\it strongly hybridized}, a feature not often seen in rare-earth-containing materials, and that the isolated Dy$_{\rm Zr}$ defect might be the source of a broad blue emission in band-to-defect ("charge-transfer") luminescence.
Submission history
From: Khang Hoang [view email][v1] Thu, 18 Nov 2021 08:07:15 GMT (3179kb)
[v2] Thu, 17 Feb 2022 15:33:53 GMT (2805kb)
Link back to: arXiv, form interface, contact.