Title: Effect of Sintering Conditions on the Microstructure and Electrochemical Properties of 6Scandia 1Ceria co-doped Zirconia (6Sc1CeZr)
(Submitted on 25 May 2022 (this version), latest version 29 Oct 2022 (v3))
Abstract: The current work studies the effect of sintering conditions on the densification behavior, microstructure, and electrochemical performance of 6 mol% Sc2O3, 1 mol% CeO2 co-doped ZrO2 (6Sc1CeZr) for solid-state electrolyte applications. The specimen's physical properties and electrochemical performance sintered at different temperatures ranging from 1000 {\deg}C to 1700 {\deg}C for 6 hours are examined through diffraction, microscopy, and Raman and electrochemical impedance spectroscopy. The activation energy and pre-exponential conductivity factor of the oxygen ions are calculated using a linear fit to the Arrhenius-type conductivity equation. We observe that samples sintered at 1500 {\deg}C for 6h show a lower c/a axial ratio for the tetragonal phase, highest relative density, and highest total conductivity among all samples investigated. The higher total conductivity is explained by the formation of a higher symmetric tetragonal phase and the simultaneous existence of the cubic and tetragonal phases (with higher symmetry), supported by the presence of the cerium ions partially replaced zirconium ions' sites.
Submission history
From: Pooya Elahi [view email][v1] Wed, 25 May 2022 09:02:35 GMT (1677kb)
[v2] Thu, 22 Sep 2022 01:17:23 GMT (0kb,I)
[v3] Sat, 29 Oct 2022 01:56:17 GMT (0kb,I)
Link back to: arXiv, form interface, contact.