Title: Superconductivity of high-entropy-alloy-type transition-metal zirconide (Fe,Co,Ni,Cu,Ga)Zr2

Abstract: We synthesized a new high-entropy-alloy-type (HEA-type) superconductor (Fe,Co,Ni,Cu,Ga)Zr2 with a Tc of 2.9 K. The EDX analyses revealed that the actual composition of the transition-metal site (Tr-site) is Tr = Fe0.18Co0.18Ni0.16Cu0.25Ga0.23, which gives the configurational entropy of mixing {\Delta}Smix = 1.60R for the Tr site. Neutron powder diffraction revealed that the sample has a tetragonal CuAl2-type (space group: #140). The lattice constant of a monotonically decreases with decreasing temperature, but the lattice constant of c does not exhibit a clear shrinkage. Isotropic displacement parameter for both the Tr and Zr sites are large, which is probably caused by the HEA-type Tr site. The small temperature dependences of Uiso for both sites also indicate the presence of the local structural disorder in (Fe,Co,Ni,Cu,Ga)Zr2. From electrical resistivity, magnetic susceptibility, and specific heat measurements, bulk superconductivity was confirmed.