Title: High temperature equilibrium of 3D and 2D chalcogenide perovskites

Abstract: Chalcogenide perovskites have been recently under the researchers spotlight as novel absorber materials for photovoltaic applications. BaZrS$_3$, the most investigated compound of this family, shows a high absorption coefficient, a bandgap of around 1.8 eV, and excellent environmental and thermal stability. In addition to the 3D perovskite BaZrS$_3$, the Ba-Zr-S compositional space contains various 2-D Ruddlesden-Popper phases Ba$_{x+1}$Zr$_x$S$_{3x+1}$ (with $x=$ 1, 2, 3) which have recently been reported. In this work it will be shown that at high temperature the Gibbs free energies of 3D and 2D perovskites are very close, suggesting that 2D phases can be easily formed at high temperatures. The analysis of the product of the BaS and ZrS$_2$ solid-state reaction, both in stoichiometric and Zr-rich conditions, present a mixture of BaZrS$_3$ and Ba$_4$Zr$_3$S$_{10}$, supporting the thermodynamic calculations result. To carefully resolve the composition, XRD, SEM and EDS analysis were complemented with Raman spectroscopy. For this purpose, the phonon modes, and the consequent Raman spectra, were calculated for the 3D and 2D chalcogenide perovskites, as well as for the binary precursors. This thorough characterization will demonstrate that the formation of 3D and 2D mixtures is thermodynamically possible, and that it is important to use of multiple techniques to soundly resolve the composition of these chalcogenide materials.