Title: Gain Recovery in Heavily Irradiated Low Gain Avalanche Detectors by High Temperature Annealing
(Submitted on 25 Jan 2023 (this version), latest version 20 Mar 2023 (v2))
Abstract: Studies of annealing at temperatures up to 450$^\circ$C with LGADs irradiated with neutrons are described. It was found that the performance of LGADs irradiated with 1.5e15 n/cm$^2$ was already improved at 5 minutes of annealing at 250$^\circ$C. Isochronal annealing for 30 minutes in 50$^\circ$C steps between 300$^\circ$C and 450$^\circ$C showed that the largest beneficial effect of annealing is at around 350$^\circ$C. Another set of devices was annealed for 60 minutes at 350$^\circ$C and this annealing significantly increased V$_{\mathrm{gl}}$. The effect is equivalent to reducing the effective acceptor removal constant by a factor of $\sim$ 4. Increase of V$_{\mathrm{gl}}$ is the consequence of increased effective space charge in the gain layer caused by formation of electrically active defects or re-activation of interstitial Boron atoms.
Submission history
From: Igor Mandić [view email][v1] Wed, 25 Jan 2023 17:52:23 GMT (2615kb,D)
[v2] Mon, 20 Mar 2023 13:17:12 GMT (2644kb,D)
Link back to: arXiv, form interface, contact.