Title: Superconducting properties of MgB2 thin films prepared on flexible plastic substrates
(Submitted on 24 Jun 2002 (v1), last revised 25 Jun 2002 (this version, v2))
Abstract: Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in an Ar or vacuum atmosphere. In the optimal annealing process, the Mg-B films were heated to approximately 600 C, but at the same time, the backside of the structures was attached to a water-cooled radiator to avoid overheating of the plastic substrate. The resulting MgB2 films were amorphous with the onset of the superconducting transition at T_(c,on) about 33 K and the transition width of approximately 3 K. The critical current density was > 7x10^5 A/cm^2 at 4.2 K, and its temperature dependence indicated a granular film composition with a network of intergranular weak links. The films could be deposited on large-area foils (up to 400 cm^2) and, after processing, cut into any shapes (e.g., stripes) with scissors or bent multiple times, without any observed degradation of their superconducting properties.
Submission history
From: Andrej Plecenik [view email][v1] Mon, 24 Jun 2002 09:07:21 GMT (75kb)
[v2] Tue, 25 Jun 2002 06:19:06 GMT (75kb)
Link back to: arXiv, form interface, contact.