Title: Magnetic and Transport Properties of La$_{0.7}$Sr$_{0.3}$Co$_{1-y}$Mn$_y$O$_3$
(Submitted on 16 Jul 2002)
Abstract: While both La$_{0.7}$Sr$_{0.3}$MnO$_3$ and La$_{0.7}$Sr$_{0.3}$CoO$_3$ are ferromagnets with metallic conductivity below $T_\mathrm{c}$ (360K and 220K, respectively), partial substitutions of Co by Mn in La$_{0.7}$Sr$_{0.3}$Co$_{1-y}$Mn$_y$O$_3$ ($y < 0.1$) drastically suppress the ferromagnetic long-range order pre-established by Co-O-Co double exchange and tune the conductivity towards insulating behavior. Since Mn-O-Mn double-exchange interactions are avoidable at low Mn-substitution levels, the deterioration of ferromagnetism and conductivity thus provides evidence for no Mn-O-Co double exchange (but antiferromagnetic superexchange) in the present system. At $y = 0.1$, the ferromagnetism is no longer observed; the system becomes an insulating spin-glass with $T_\mathrm{g}\approx 62$K as estimated from the ac-susceptibility data using the conventional critical slowing-down scaling law. With further substitution ($y\geq 0.3$), the ferromagnetism is recovered ($T_\mathrm{c} = 165$K for $y = 0.3$ and 200K for $y = 0.5$) while the resistivity continues increasing and exhibits insulating behavior. These results indicate that the substitution is not simply a mixture of La$_{0.7}$Sr$_{0.3}$MnO$_3$ and La$_{0.7}$Sr$_{0.3}$CoO$_3$, but produces a more complicated scenario of spin states, interactions and disorder.
Link back to: arXiv, form interface, contact.