Title: Spin structure and magnetic phase transitions in TbBaCo2O5.5

Abstract: Spin ordering in TbBaCo2O5.5 and its temperature transformation is studied. First of all, the polymorphism that depends on the oxygen ordering at the same average content is investigated. One of two differently treated powder samples (I) had, in addition to the main phase TbBaCo2O5.45(2) (ap x 2ap x 2ap, Pmmm), about 25% of TbBaCo2O5.51(3) with statistical distribution of oxygen over the apical sites (ap x ap x 2ap, Pmmm), where ap is parameter of perovskite cell. The other (II) contained a single phase TbBaCo2O5.54(2) (ap x 2ap x 2ap, Pmmm) with well defined octahedral and pyramidal sublattices. Treatment of neutron diffraction patterns of the sample I itself gives a sophisticated spin structure. Knowing the structure of sample II, one can chose only proper magnetic lines, which give exactly the same results as for sample II. Above the Neel temperature TN ~ 290 K there is a structure transition to the phase 2ap x 2ap x 2ap, Pmma. The spins order with the wave vector k19 = 0 (Phase 1). At T1 \~ 255 K there is a magnetic transition to the phase 2 with k22 = b3/2. At T2 ~ 170 K the crystal structure changes to 2ap x 2ap x 4ap, Pcca. The wave vector of the spin structure becomes again k19 = 0 (Phase 3). The basis functions of irreducible representations of the group Gk have been found. With this analysis the magnetic structure in all phases is determined. The spins are always parallel to the x axis, and the difference is in the moment value and direction in the ordered non-equivalent pyramidal or octahedral positions. Spontaneous moment at T = 260 K is due to ferrimagnetic ordering of the moments in pyramidal sites. (Dzyaloshinskii-Moriya canting is forbidden by symmetry.) The moment values together with the ligand displacements are used to analyze the picture of spin-state/orbital ordering in each phase.