Condensed Matter > Superconductivity

Title: Superconductivity with Tc=7 K under pressure for Cu-, and Au-doped BaFe2As2

Abstract: It is noteworthy that chemical substitution of BaFe2As2 (122) with the noble elements Cu and Au gives superconductivity with a maximum Tc=3 K, while Ag substitution (Ag-122) stays antiferromagnetic. For Ba(Fe1-xTMx)2As2, TM= Cu, Au, or Ag, and by doping an amount of x=0.04, a-lattice parameter slightly increases (0.4%) for all TM dopants, while c-lattice decreases (-0.2%) for TM=Cu, barely moves (0.05%) for Au, and increases (0.2%) for Ag. Despite the naive expectation that the noble elements of group 11 should affect the quantum properties of 122 similarly, they produce significant differences extending to the character of the ground state. For the Ag-122 crystal, evidence of only a filamentary superconductivity is noted with pressure. However, for Au and Cu doping (x=0.03) we find a substantial improvement in the superconductivity, with Tc increasing to 7 K and 7.5 K, respectively, under 20 kbar of pressure. As with the ambient pressure results, the identity of the dopant therefore has a substantial impact on the ground state properties. Density functional theory calculations corroborate these results and find evidence of strong electronic scattering for Au and Ag dopants, while Cu is comparatively less disruptive to the 122 electronic structure.
Subjects: Superconductivity (cond-mat.supr-con)
DOI: 10.1088/1361-648X/ab7e60
Cite as: arXiv:2002.04662 [cond-mat.supr-con]
  (or arXiv:2002.04662v1 [cond-mat.supr-con] for this version)

Submission history

From: Athena Sefat S. [view email]
[v1] Tue, 11 Feb 2020 20:16:47 GMT (946kb)

Link back to: arXiv, form interface, contact.