# Title: On the Elasticity of Polymer Model Networks Containing Finite Loops

(Submitted on 30 Mar 2021)

Abstract: Based upon the resistor analogy and using the ideal loop gas approximation(ILGA) it is shown that only pending loops reduce the modulus of an otherwise perfect network made of monodisperse strands and junctions of identical functionality. Thus, the cycle rank of the network with pending structures removed (cyclic and branched) is sufficient to characterize modulus, if the resistor analogy can be employed. It is further shown that it is impossible to incorporate finite cycles into a polymer network such that individual network strands are at equilibrium conformations while maintaining simultaneously a force balance at the junctions. Therefore, the resistor analogy provides only an approximation for the phantom modulus of networks containing finite loops. Improved approaches to phantom modulus can be constructed from considering a force balance at the junctions, which requires knowledge of the distribution of cross-link fluctuations in imperfect networks. Assuming loops with equilibrium conformations and a force balance at all loop junctions, a lower bound estimate for the phantom modulus, $G_{\text{ph}}\approx\left(\xi-c_{\text{f}}L_{1}\right)kT/V$ is obtained within the ILGA for end-linked model networks and in the limit of $L_{1}\ll\xi$. Here, $L_{1}$ is the number of primary ("pending") loops, $\xi$ the cycle rank of the network, $k$ the Boltzmann constant, $V$ the volume of the sample, and $T$ the absolute temperature. $c_{\text{f}}$ is a functionality dependent coefficient that is $\approx2.56$ for junction functionality $f=3$ and $\approx3.06$ for $f=4$, while it converges quickly towards $\approx4.2$ in the limit of large $f$. Further corrections to phantom modulus beyond finite loops are addressed briefly.

Link back to: arXiv, form interface, contact.