Title: Isochronal annealing effects on local structure, crystalline fraction, and undamaged region size of radiation damage in Ga-stabilized $δ$-Pu
(Submitted on 11 Feb 2016 (this version), latest version 14 Apr 2016 (v2))
Abstract: The effects on the local structure due to self-irradiation damage of Ga stabilized $\delta$-Pu stored at cryogenic temperatures have been examined using extended X-ray absorption fine structure (EXAFS) experiments. Extensive damage, seen as a loss of local order, was evident after 72 days of storage below 15 K. The effect was observed from both the Pu and Ga sites, although less pronounced around Ga. Isochronal annealing was performed on this sample to study the annealing processes that occur between cryogenic and room temperature storage conditions, where damage is mostly reversed. Damage fractions at various points along the annealing curve have been determined using amplitude ratio techniques, standard EXAFS fitting, and a spherical crystallite model. The use of a spherical crystallite model can provide information complementary to resistivity and susceptibility based annealing studies, and can account for the changes in EXAFS spectra using just two parameters. These results are discussed in terms of changes to the local structure around Ga and Pu throughout the annealing process.
Submission history
From: Daniel Olive [view email][v1] Thu, 11 Feb 2016 22:04:23 GMT (360kb,D)
[v2] Thu, 14 Apr 2016 23:31:00 GMT (308kb,D)
Link back to: arXiv, form interface, contact.